| JM-1 |
Gunmetal |
|
Cu |
Sn |
Pb |
Zn |
Ni |
Al |
Fe |
Mn |
Densit |
0,2 limit |
Breaking tenacity |
Strain |
Hardness |
Other standards |
| -15 |
Most economic and mostly used sliding bearings for common use. Good wear resistance and sliding qualities. |
|
85 |
5 |
5 |
5 |
|
|
|
|
8,8 |
100-130 |
250-290 |
13-20 |
70-80 |
SS5204-15, BS1400LG2, SFS GZ-CuPb5Sn5Zn5 |
| -03 |
Not recommended for sliding bearings when sand cast, and not seawater resistant. |
|
85 |
5 |
5 |
5 |
|
|
|
|
8,8 |
90 |
230 |
15 |
60 |
SS5204-03, DIN 1705-G-CuSn5ZnPb, SFS G-CuPb5Sn5Zn5 |
| JM-2 |
Tin bronze |
|
Cu |
Sn |
Pb |
Zn |
Ni |
Al |
Fe |
Mn |
Density |
0,2 limit |
Breaking tenacity |
Strain |
Hardness |
Other standards |
| -15 |
Great tenacity, combined with the best wear resistance.Recommended when staying within the dimension under impact and heavy loads is a requirement. Does not conform to edge loading. Mating material preferably hard and quenched. Good salt water resistance. |
|
90 |
10 |
|
|
|
|
|
|
8,8 |
130-170 |
270-330 |
18-25 |
70-90 |
SS5443-15, SFS GZ-CuSn10 |
| -03 |
Due to wear resistance the best sand cast alloys are alloys with plenty of tin (14%) |
|
90 |
10 |
|
|
|
|
|
|
8,8 |
130 |
270 |
18 |
70 |
SS5443-03, DIN 1705-G-CuSn10, SFS G-CuSn10 |
| JM-3 |
Tin Bronze |
|
Cu |
Sn |
Pb |
Zn |
Ni |
Al |
Fe |
Mn |
Density |
0,2 limit |
Breaking tenacity |
Strain |
Hardness |
Other standards |
| -15 |
Great tenacity combined with the best wear resistance. Recommended when staying within the dimension under impact and heavy loads is a requirement. Does not conform to edge loading. Mating material preferably hard and quenched. Good salt water resistance. |
|
88 |
12 |
|
|
|
|
|
|
8,8 |
180-185 |
300-310 |
8-12 |
105-110 |
SS5443-15, SFS GZ-CuSn10 |
| -03 |
Due to wear resistance the best sand cast alloys are alloys with plenty of tin (14%) |
|
88 |
12 |
|
|
|
|
|
|
8,8 |
160 |
280 |
12 |
95 |
SS5443-03, DIN 1705-G-CuSn10, SFS G-CuSn10 |
| JM-4 |
Leaded tin bronze |
|
Cu |
Sn |
Pb |
Zn |
Ni |
Al |
Fe |
Mn |
Density |
0,2 limit |
Breaking tenacity |
Strain |
Hardness |
Other standards |
| -15 |
When lubrication is intermittent or otherwise insufficient, these bearing bronzes have the best wear resistance and sliding properties. The bearing bronzes most suitable for water lubrication. Conforms to edge loading and have good saltwater resistance. |
|
77 |
8 |
15 |
|
|
|
|
|
9,1 |
100 |
220 |
4 |
65 |
DIN1716 GZ-CuPb15Sn8, SFS GZ-CuPb15Sn8 |
| -03 |
Noticeably poorer wear resistance |
|
77 |
8 |
15 |
|
|
|
|
|
9,1 |
80 |
170 |
5 |
60 |
DIN 1716 G-CuPb15Sn, SFS G-CuPb15Sn |
| JM-5 |
LEADED TIN BRONZE |
|
Cu |
Sn |
Pb |
Zn |
Ni |
Al |
Fe |
Mn |
Density |
0,2 limit |
Breaking tenacity |
Strain |
Hardness |
Other standards |
| -15 |
When lubrication is intermittent or otherwise insufficient these bearing bronzes have the best wear resistance and sliding properties. The best suitable bearing bronzes for water lubrication. Conforms to edge loading and have good saltwater resistance. |
|
80 |
10 |
10 |
|
|
|
|
|
8,9 |
110-145 |
220-260 |
6-14 |
70-85 |
SS5640-15, DIN1716 GZ-CuPb10Sn |
| -03 |
Noticeably poorer wear resistance |
|
80 |
10 |
10 |
|
|
|
|
|
8,9 |
80 |
180 |
7 |
65 |
SFS GZ-CuPb10Sn10 |
| JM-6 |
Aluminum bronze |
|
Cu |
Sn |
Pb |
Zn |
Ni |
Al |
Fe |
Mn |
Density |
0,2 limit |
Breaking tenacity |
Strain |
Hardness |
Other standards |
| -15 |
Material possesses great tenacity and high corrosion resistance. Sliding properties and wear resistance clearly poorer than above mentioned alloys. Only recommended for sliding bearings when yield properties of tin bronze are insufficient. Good saltwater resistance. |
|
87 |
|
|
|
|
10 |
3 |
|
7 |
200 |
550 |
15 |
115 |
SS5710-15, BS1400AB1, SFS GZ-CuAl10Fe3 |
| -03 |
Same properties |
|
87 |
|
|
|
|
10 |
3 |
|
7 |
180 |
550 |
13 |
115 |
SS5710-03, DIN 1714 G-CuAl10Fe |
| JM-7 |
Aluminum bronze |
|
Cu |
Sn |
Pb |
Zn |
Ni |
Al |
Fe |
Mn |
Density |
0,2 limit |
Breaking tenacity |
Strain |
Hardness |
Other standards |
| -15 |
Material possessing great tenacity and high corrosion resistance. Sliding properties and wear resistance clearly poorer than above mentioned alloys. Only recommended in slide bearings when yield properties of tin bronze are insufficient. Good saltwater resistance. |
|
80 |
|
|
|
5 |
10 |
4 |
1 |
7,6 |
250-320 |
670-680 |
13-15 |
160-170 |
DIN 1714 GZ/GC-Al10Ni |
| -03 |
Same properties |
|
80 |
|
|
|
5 |
10 |
4 |
1 |
7,6 |
250 |
640 |
13 |
140 |
DIN 1714 G-CuAl10Ni, SFS G-CuAl10Fe5NI5 |
| -20 |
Same properties |
|
80 |
|
|
|
5 |
10 |
4 |
1 |
7,6 |
270-310 |
630-680 |
13-15 |
170-210 |
DIN 17672 G-CuAl10Ni |
| JM-15 |
Manganese bronze |
|
Cu |
Sn |
Pb |
Zn |
Ni |
Al |
Fe |
Mn |
Density |
0,2 limit |
Breaking tenacity |
Strain |
Hardness |
Other standards |
| -15 |
Material possessing great tenacity and high corrosion resistance. Sliding properties and wear resistance clearly poorer than above mentioned alloys. Only recommended in slide bearings when yield properties of tin bronze are insufficient. Good saltwater resistance. |
|
60 |
|
|
jäännös |
1 |
1,5 |
1 |
1,5 |
8,2 |
200 |
500 |
18 |
120 |
DIN 1709 GZ/GC-CuZn35Al1 |
| -03 |
Same properties |
|
60 |
|
|
jäännös |
1 |
1,5 |
1 |
1,5 |
8,2 |
170 |
500 |
20 |
110 |
DIN 1709 G-CuZn35A11, SFS G-CuZn35AlFeMn |